NOMENCLATURE		SPECIFICATIONS-CROSS REF.					CHEMICAL COMPOSITION				PERCENT MAX.		EXCEPT AS INDICATED					MECHANICAL PROPERTIES
	INGOT #	COPPER ALLOY UNS NO.q	A.S.T.M.	FORMER S.A.E. #	FEDERAL	MILITARY	COPPER	TIN	LEAD	ZINC	NICKEL INCL. COBALT	IRON	SILICON	ALUMINUM	ANTIMONY	PHOSPHORUS	SULFUR	TENSILE STRENGTH P.S.I.	YIELD STRENGTH P.S.I.	ELONGATION IN 2 IN. PERCENT	BRINELL HARDNESS	POURING TEMPERATURE RANGE *F
																		MIN.	MIN.	MIN.	TYPICAL	LIGHT CASTINGS	HEAVY CASTINGS
LEADED RED BRASS
		C83450	B30-83				87-89	2.2-3.0	1.5-2.5	5.8-7.5	0.8-1.5	0.25	0.005	0.005	0.25	0.03	0.08
85-5-5-5	115	C83600	B584-83				87-89	2.0-3.5	1.5-3.0	5.5-7.5	.75-2.0	0.30	0.005	0.005	0.25	0.05	0.08	30,000	14,000	25	55-65	2100-2350	1950-2150
			B62-82a	40	QQ-C-390A	MIL-C-11866C MIL-C-15345G1-1 MIL-C-22087A MIL--C-22229A	84-86	4.0-6.0	4.0-6.0	4.0-6.0	1.0+	0.30	0.005	0.005	0.25	0.05	0.08	30,000	14,000	20	55-65	2100-2350	1950-2150
TIN BRONZE
88-8-4/Navy "G"	225	C90300	B30-83				86-89	7.8-9.0	0.25	3.5-5.0	.8+	0.15	0.005	0.005	0.20	0.03	0.05
					QQ-C-525b-5		86-89	7.8-9.0	0.25	3.5-5.0	.8+	0.20	0.005	0.005	0.25	0.03	0.05					2000-2300	1900-2100
			B271-81	620	QQ-C-390A	MIL-C-11866C	86-89	7.5-9.0	0.30	3.0-5.0	1.0+	0.15	0.005	0.005	0.20	0.05	0.05	40,000	18,000	20	60-75
			B584-83			MIL-C-15345G1-8												(44,000)	(18,000)	(18)
						MIL-C-22087Ae
88-10-2/Gun Metal	210	C90500	B271-81	62			86-89	9.0-11.0	0.30	1.0-3.0	1.0+	0.20	0.005	0.005	0.20	0.05	0.05	40,000	18,000	20	75-85	2000-2300	1900-2100
			B584-83
			B505-2a
89-11 Phos.Gear	205	C90700		65	QQ-C-390A		88-89	10.0-12.0	0.50	0.50	0.50	0.15	0.005	0.005	0.20	0.30	0.05	35,000	18,000	10		1900-2000	1800-1900
Bronze			B505-82a				88-89	10.-12.0	0.50	0.50	0.50	0.15	0.005	0.005	0.10	1.5	0.05
Bearing Bronze	197	C91000	B505-82a		QQ-C-390A		84-86	14.0-16.0	0.20	1.50	0.80	0.10	0.005	0.005	0.20	0.10	0.05	30,000		1		2100-2300	1900-2100
Bearing Bronze		C91100	B22-82				82-85	15.0-17.0	0.25	0.25	0.50	0.25	0.005	0.005	0.20	0.10	0.05	Deformation Limit, Min.p.s.i.-18,000; Permanent Set in 1 in. under 10,000 p.s.i., in 0.10 -0.20 for B22-82 only.
		NOTE: ANCHOR CASTINGS ALSO POUR C91600 UPON SPECIAL REQUESTS
LEADED TIN BRONZE
88-6-2-4 Navy "M"	245	C92200	B271-81	622	QQ-C-390A	MIL-C-15345G1-9 (Copper 86-89)	86+-90	5.5-6.5	1.0-2.0	3.0-5.0	1.0+	0.25	0.005	0.005	0.25	0.05	0.05	34,000	16,000	24	60-72	2000-2300	1900-2150
			B584-83
			B61-82
			B505-82a				86-89	5.5-6.5	1.0-2.0	3.0-5.0	1.00	0.25	0.005	0.005	0.25	1.50	0.05	34,000	16,000	22
Leaded Gun Metal	206	C92700		63	QQ-C-390A		86-89	9.0-11.0	1.0-2.5	0.07	1.00	0.20	0.005	0.005	0.25	0.25	0.05	35,000	18,000	10		2100-2300	1920-2100
LEADED YELLOW BRASS
High Copper	400	C85200	B271-81			MIL-C-11866C	70-74	.7-2.0	1.5-3.8	20-27	1.00	0.60	0.05	0.005	0.20	0.01	0.05	35,000	12,000	25		2000-2100	1850-2000
			B584-83		QQ-C-390A		70-74	.8-2.0	1.5-3.7	Remainder		0.60
MANGANESE BRONZE																MANGANESE
High Strength Yellow Brass (Manganese Bronze)110,000	424	C86300	B22-82	430B		MIL-C-11866C	60-66	0.20	0.20	22-28	1.00	2.0-4.0		5.0-7.5	NO ANTIMONY OR PHOSPHORUS	MANGANESE 2.5-5.0		110,000	60,000	12	217-269	1950-2050	1850-1950
			B271-81
			B584-83
			B505-82a
	NOTE: ANCHOR CASTINGS ALSO POURS C865/MANGANESE BRONZE (65,000)
SILICON BRONZE AND BRASS																MANGANESE
SILICON BRASS	500	C87500	B271-81				79 MIN.		0.5	12.0-16.0			3.0-5.0	0.5	NO ANTIMONY OR PHOS.	NONE		60,000	24,000	16		2000-2150	1900-2000
			B584-83
		C87600	B584-83				88 MIN.		0.5	4.0-7.0			3.5-5.5			NONE		60,000	30,000	16	110
ALUMINUM BRONZE AND NICKEL/ALUMINUM/BRONZE																MANGANESE
ALUM/BRZ	415	C95200	B148-82	68A	QQ-C-390A	MIL-C-22229A	,000					2.5-4.0		8.5-9.5	NO ANTIMONY OR PHOS.	NONE		65,000 AS CAST	25,000 AS CAST	20	110	2050-2300	1950-2150
			B271-81			MIL-C-22087A
		C95300	B148-82	68B	QQ-C-390A	MIL-C-11866C	86 MIN.					.75-1.5		9.0-11.0	NO ANTIMONY OR PHOS.	NONE		65,000 AS CAST OR 80,000 HEAT TREATED	25,000 AS CAST OR 40,000 HEAT TREATED	20 AS CAST	110 A.C. OR 160 H.T.
			B271-81																	12 HEAT TRT.
		C95400	B148-82		QQ-C-390A	MIL-C-11866C	83 MIN.					3.0-5.0		10.0-11.5	NO ANTIMONY OR PHOS.	MANGANESE		75,000 A.C. OR 90,000 H.T.	30,000 A.C. OR 45,000 H.T.	12 A.C.	150 A.C. OR 190 H.T.
			B271-81													0.50				6 H.T.
NI/ALUM/BRZ	415D	C95500	B148-82		QQ-C-390A	MIL-C-22087A	78 MIN.				3.0-5.5	3.0-5.0		10.0-11.5	NO ANTIMONY OR PHOS.	MANGANESE		90,000 A.C. OR 110,000 H.T.	40,000 A.C. OR 60,000 H.T.	6 A.C.	175-210 A.C. OR 215-260 H.T.
			B271-81			MIL-C-22229A										3.5				5 H.T.
		C95800	B271-81		QQ-C-390A	MIL-B-24480(SHIPS)	79 MIN.		0.03		4.0-5.0	3.5-4.5	0.10	8.5-9.5	NO ANTIMONY OR PHOS.	MANGANESE		85,0000 MINIMUM OR 105,000 IF H.T.	35,000 MINIMUM OR 62,500 IF H.T.	15-18
			B148-82													.8-1.5
			B505-82a
ALUMINUM ALLOYS		LISTED BELOW ARE THE ALLOYS WE POUR IN ALUMINUMÉMORE DATA TO COME SOON!
A319		NO HEAT TREAT
A355				MORE INFORMATION TO COME SOON.
A356
713 TENZALLOY		HI TENSILE
A356 PRIMARY
ALMAG 35